mn doped zno nanocomposite thin film coated on glass by a simple spin-coating method was used to degrade an azo textile dye from aqueous environment. mn doped zno nanocomposite thin film was characterized by means of x-ray diffraction (xrd) and scanning electron microscopy (sem). the photo-reduction activity of photocatalyst was evaluated using an azo textile dye as organic contaminant irradiat...

Mn doped ZnO nanocomposite thin film coated on glass by a simple spin-coating method was used to degrade an azo textile dye from aqueous environment. Mn doped ZnO nanocomposite thin film was characterized by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photo-reduction activity of photocatalyst was evaluated using an azo textile dye as organic contaminant irradiat...

Mn doped ZnO nanocomposite thin film coated on glass by a simple spin-coating method was used to degrade an azo textile dye from aqueous environment. Mn doped ZnO nanocomposite thin film was characterized by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photo-reduction activity of photocatalyst was evaluated using an azo textile dye as organic contaminant irradiat...

The charge state and local ordering of Mn doped into a pulsed laser deposited single-phase thin film of ZnO are investigated by using x-ray absorption spectroscopy at the O K-edge, Mn K-edge and L-edge, and x-ray emission spectroscopy at the O K-edge and Mn L-edge. This film is ferromagnetic at room temperature. EXAFS measurement shows that Mn(2+) replaces the Zn site in tetrahedral symmetry, a...

N-doped ZnO thin films were deposited on n-type Si(100) and homo-buffer layer, and undoped ZnO thin film was also deposited on homo-buffer layer by RF magnetron sputtering method. After deposition, all films were in-situ annealed at 800 C for 5 minutes in ambient of O2 with pressure of 10 Torr. X-ray diffraction shows that the homobuffer layer is beneficial to the crystalline of N-doped ZnO thi...

This paper reports the growth of Mn doped ZnO thin films by sol-gel technique with different Mn concentration (0-20 %). Structural and vibrational properties have been measured by X-ray diffraction and Raman spectroscopy. The films exhibit crystalline nature with (002) preferential orientation. The crystallite size and lattice parameters have been estimated as a function of Mn concentration. Th...

A Silver (Ag) thin film is introduced as a template and doping source for vertically aligned p–type ZnO nanorods. ZnO nanorods were grown using an ammonium hydroxide based hydrothermal process. During the hydrothermal process, the Ag thin film was dissolved to generate Ag ions in the solution. The Ag ions can contribute to doping in the wurzite structure of ZnO and the (111) grain of Ag thin fi...

We report the synthesis of colloidal Mn(2+)-doped ZnO (Mn(2+):ZnO) quantum dots and the preparation of room-temperature ferromagnetic nanocrystalline thin films. Mn(2+):ZnO nanocrystals were prepared by a hydrolysis and condensation reaction in DMSO under atmospheric conditions. Synthesis was monitored by electronic absorption and electron paramagnetic resonance (EPR) spectroscopies. Zn(OAc)(2)...

Thin film of zinc oxide was prepared by spin coating on pyrex glass using zinc acetate dehydrate, 2-methoxyethanol and monoethanolamine (MEA) as a precursor, solvent and stabilizer respectively. Also, Aluminium-doped thin film of ZnO was prepared by using AlCl3. Deposited thin films were investigated for structural and optical properties using X-ray diffraction (XRD) and UV–VIS-NIR spectrophoto...

Thin film of zinc oxide was prepared by spin coating on pyrex glass using zinc acetate dehydrate, 2-methoxyethanol and monoethanolamine (MEA) as a precursor, solvent and stabilizer respectively. Also, Aluminium-doped thin film of ZnO was prepared by using AlCl3. Deposited thin films were investigated for structural and optical properties using X-ray diffraction (XRD) and UV–VIS-NIR spectrophoto...